Cloud point-resistant adhesives and laminates

ABSTRACT

Optically clear adhesives and laminates that include the adhesives are provided. The adhesives and laminates remain haze-free and are cloud point-resistant when placed in environments of high humidity and elevated temperature. The adhesives and laminates are useful in optical electronic display applications.

FIELD

The present disclosure relates to optically clear adhesives andlaminates that include the adhesives.

BACKGROUND

Optically clear pressure sensitive adhesives (OCAs) are finding wideapplications in optical displays. Such applications include bondingpolarizers to modules of a liquid crystal display (LCD) and attachingvarious optical films to a glass lens in, for example, mobile hand held(MHH) devices. During use, the display can be subjected to variousenvironmental conditions, such as high temperature and/or high humidity.

It has been observed that OCAs can exhibit a cloud point, (turnhazy/“white”) after subjecting optical laminates of optical films andOCAs to high temperature/humidity accelerated aging tests andsubsequently cooling the laminates down to ambient conditions. Whilestill hot, the laminates may be perfectly clear, even when saturatedwith moisture. But upon cooling they can exhibit a cloud point and turnhazy or “white”. Frequently, the haze will disappear over time uponstorage of the laminate under ambient conditions. The haze disappearancecan often be accelerated by gently heating the optical laminates.

SUMMARY

There is a need for OCAs that remain clear and defect free whenincorporated into optical displays, such as LCDs. There is a need forcloud point-resistant adhesives and laminates that do not become hazywhen subjected to various environmental conditions such as temperatureand humidity changes.

In one aspect, an optically clear laminate is provided that includes afirst substrate having at least one major surface, a second substratehaving at least one major surface, and a cloud point-resistant,optically clear adhesive composition situated between and in contactwith at least one major surface of the first substrate and at least onemajor surface of the second substrate, wherein the adhesive compositionis derived from precursors that include from about 75 to about 95 partsby weight of an alkyl acrylate having 1 to 14 carbon in the alkyl group,from 0 to about 5 parts of a copolymerizable polar monomer; and fromabout 1 to about 25 parts of a hydrophilic polymeric compound based upon100 parts of the alkyl acrylate and the copolymerizable polar monomer.

In another aspect, an optically clear laminate is provided that includesa first substrate having at least one major surface, a second substratehaving at least one major surface; and a cloud point-resistant,optically clear adhesive composition situated between and in contactwith at least one major surface of the first substrate and at least onemajor surface of the second substrate, wherein the adhesive compositionis derived from precursors that include from about 60 to about 95 partsby weight of an alkyl acrylate having 1 to 14 carbon atoms in the alkylgroup, from 0 to about 5 parts of a copolymerizable polar monomer, andfrom about 5 to about 50 parts of a hydroxyl-containing monomer that hasan OH equivalent weight of less than 400.

In yet another aspect, an optically clear adhesive composition isprovided that is derived from precursors that comprise from about 75 toabout 95 parts by weight of an alkyl acrylate having 1 to 14 carbon inthe alkyl group, from 0 to about 5 parts of a copolymerizable polarmonomer, and from about 1 to about 25 parts of a hydrophilic polymericcompound based upon 100 parts of the alkyl acrylate and thecopolymerizable polar monomer.

By incorporating hydrophilic moieties in the OCA matrix, haze-free,cloud point-resistant OCAs can be obtained which remain clear even afterhigh temperature/humidity accelerated aging tests. The provided OCA'sare suitable for use in, for example, laminating polarizers to opticalLCDs, attaching various optical films to glass lenses in mobile handhelddevices, and other adhesive application that require optical clarity invarious temperature and humidity environments.

Although not wishing to be bound by theory, it is thought that the hazeappears when the OCA becomes saturated with water at elevatedtemperatures, and the concentration of water exceeds the cloud pointwhen quickly cooled due to poor compatibility of the moisture with theOCA matrix. This can result in localized phase separation of small waterdroplets, which due to a mismatch in refractive index with the OCAmatrix, causes haze or a “white” appearance. If the droplets remain verysmall (e.g., a few hundred nanometers or less) or the water remainsfully solubilized in the adhesive under ambient conditions, the OCA willstay clear while it re-equilibrates its moisture content with theenvironment.

As used herein:

“cloud point” refers to the temperature at which a mixture of adhesiveand water separate into a continuous adhesive phase and a dispersedwater phase, where the dispersed phase is larger than the wavelength oflight and thus make the adhesive appear “white” or cloudy;

“(meth)acrylate” or “(meth)acrylic” refers to either the acid or theester or amide derivative of acrylic acid or methacrylic acid;

“white” or “cloudy” refers to an adhesive or laminate that is highlytranslucent so that it is difficult or impossible to visually observe animage though the adhesive or laminate;

BRIEF DESCRIPTION OF THE DRAWINGS

FIG. 1 is a cross section of a laminate of an optical film, a substrateand an embodied adhesive.

DETAILED DESCRIPTION

In the following description, reference is made to the accompanying setof drawings that form a part of the description hereof and in which areshown by way of illustration several specific embodiments. It is to beunderstood that other embodiments are contemplated and may be madewithout departing from the scope or spirit of the present disclosure.The following detailed description, therefore, is not to be taken in alimiting sense.

Unless otherwise indicated, all numbers expressing feature sizes,amounts, and physical properties used in the specification and claimsare to be understood as being modified in all instances by the term“about.” Accordingly, unless indicated to the contrary, the numericalparameters set forth in the foregoing specification and attached claimsare approximations that can vary depending upon the desired propertiessought to be obtained by those skilled in the art utilizing theteachings disclosed herein. The use of numerical ranges by endpointsincludes all numbers within that range (e.g. 1 to 5 includes 1, 1.5, 2,2.75, 3, 3.80, 4, and 5) and any range within that range.

An optically clear laminate is provided. The laminate includes a firstsubstrate having at least one major surface, a second substrate havingat least one major surface and a cloud point-resistant, optically clearadhesive composition. By cloud point-resistant it is meant that theadhesive composition, which is initially optically clear, remainsoptically clear after exposure to high temperature and humidityenvironments and subsequent cooling to ambient conditions. Opticallyclear adhesives are commonly used to mount optical films, such aspolarizers or retardation plates, to substrate displays, such as liquidcrystal cells in LCD applications. As such, the OCA is used to laminatethe film to the substrate display to form an optically clear laminate.When used in a laminate, a cloud point-resistant, optically clearadhesive allows the laminate to remain virtually haze free or clearafter exposure to nonambient temperature and humidity conditions.

The provided adhesive compositions incorporate hydrophilic moieties intothe OCA to obtain haze-free optical laminates that remain haze-free evenafter high temperature/humidity accelerated aging tests. In one aspect,the provided adhesive compositions are derived from precursors thatinclude from about 75 to about 95 parts by weight of an alkyl acrylatehaving 1 to 14 carbon in the alkyl group. The alkyl acrylate can includealiphatic, cycloaliphatic, or aromatic alkyl groups. Useful alkylacrylates (i.e., acrylic acid alkyl ester monomers) include linear orbranched monofunctional acrylates or methacrylates of non-tertiary alkylalcohols, the alkyl groups of which have from 1 up to 14 and, inparticular, from 1 up to 12 carbon atoms. Useful monomers include, forexample, 2-ethylhexyl(meth)acrylate, ethyl(meth)acrylate,methyl(meth)acrylate, n-propyl(meth)acrylate, isopropyl(meth)acrylate,pentyl(meth)acrylate, n-octyl(meth)acrylate, isooctyl(meth)acrylate,isononyl(meth)acrylate, n-butyl(meth)acrylate, isobutyl(meth)acrylate,hexyl(meth)acrylate, n-nonyl(meth)acrylate, isoamyl(meth)acrylate,n-decyl(meth)acrylate, isodecyl(meth)acrylate, dodecyl(meth)acrylate,isobomyl(meth)acrylate, cyclohexyl(meth)acrylate, phenylmeth(acrylate),benzylmeth(acrylate), and 2-methylbutyl(meth)acrylate, and combinationsthereof.

The provided adhesive composition precursors also include from about 0to about 5 parts of a copolymerizable polar monomer such as acrylicmonomer containing carboxylic acid, amide, urethane, or urea functionalgroups. Weak polar monomers like N-vinyl lactams may also be included. Auseful N-vinyl lactam is N-vinyl caprolactam. In general, the polarmonomer content in the adhesive can include less than about 5 parts byweight or even less than about 3 parts by weight of one or more polarmonomers. Polar monomers that are only weakly polar may be incorporatedat higher levels, for example 10 parts by weight or less. Usefulcarboxylic acids include acrylic acid and methacrylic acid. Usefulamides include N-vinyl caprolactam, N-vinyl pyrrolidone,(meth)acrylamide, N-methyl(meth)acrylamide, N,N-dimethyl acrylamide,N,N-dimethyl meth(acrylamide), and N-octyl(meth)acrylamide.

The provided adhesive compositions also include from about 1 to about 25parts of a hydrophilic polymeric compound based upon 100 parts of thealkyl acrylate and the copolymerizable polar monomer. The hydrophilicpolymeric compound typically has a average molecular weight (M_(n)) ofgreater than about 500, or greater than about 1000, or even higher.Suitable hydrophilic polymeric compounds include poly(ethylene oxide)segments, hydroxyl functionality, or a combination thereof. Thecombination of poly(ethylene oxide) and hydroxyl functionality in thepolymer needs to be high enough to make the resulting polymerhydrophilic. By “hydrophilic” it is meant that the polymeric compoundcan incorporate at least 25 weight percent of water without phaseseparation. Typically, suitable hydrophilic polymeric compounds maycontain poly(ethylene oxide) segments that include at least 10, at least20, or even at least 30 ethylene oxide units. Alternatively, suitablehydrophilic polymeric compounds include at least 25 weight percent ofoxygen in the form of ethylene glycol groups from poly(ethylene oxide)or hydroxyl functionality based upon the hydrocarbon content of thepolymer. Useful hydrophilic polymer compounds may be copolymerizable ornon-copolymerizable with the adhesive composition, as long as theyremain miscible with the adhesive and yield an optically clear adhesivecomposition. Copolymerizable, hydrophilic polymer compounds include, forexample, CD552, available from Sartomer Company, Exton, Pa., which is amonofunctional methoxylated polyethylene glycol (550) methacrylate, orSR9036, also available from Sartomer, that is an ethoxylated bisphenol Adimethacrylate that has 30 polymerized ethylene oxide groups between thebisphenol A moiety and each methacrylate group. Other examples includephenoxypolyethylene glycol acrylate available from Jarchem IndustriesInc., Newark, N.J. Other examples of polymeric hydrophilic compoundsinclude poly acrylamide, poly-N,N-dimethylacrylamide, andpoly-N-vinylpyrrolidone.

In another aspect, the provided laminates include adhesive compositionsderived from precursors that include from about 60 parts by weight toabout 95 parts by weight of an alkyl acrylate having 1 to 14 carbon inthe alkyl group and from about 0 parts by weight to about 5 parts byweight of a copolymerizable polar monomer. The alkyl acrylate and thecopolymerizable polar monomer are described above. The precursors alsoinclude from about 5 parts by weight to about 50 parts by weight of ahydrophilic, hydroxyl functional monomeric compound based upon 100 partsof the alkyl acrylate and the copolymerizable polar monomer or monomers.The hydrophilic, hydroxyl functional monomeric compound typically has ahydroxyl equivalent weight of less than 400. The hydroxyl equivalentmolecular weight is defined as the molecular weight of the monomericcompound divided by the number of hydroxyl groups in the monomericcompound. Useful monomers of this type include 2-hydroxyethyl acrylateand methacrylate, 3-hydroxypropyl acrylate and methacrylate,4-hydroxybutyl acrylate and methacrylate, 2-hydroxyethylacrylamide, andN-hydroxypropylacrylamide. Additionally, hydroxy functional monomersbased on glycols derived from ethylenoxide or propyleneoxide can also beused. An example of this type of monomer includes an hydroxyl terminatedpolypropylene glycol acrylate, available as BISOMER PPA 6 from Cognis,Germany. Diols and triols that have hydroxyl equivalent weights of lessthan 400 are also contemplated for the hydrophilic monomeric compound.

The pressure sensitive adhesive can be inherently tacky. If desired,tackifiers can be added to the precursor mixture before formation of thepressure sensitive adhesive. Useful tackifiers include, for example,rosin ester resins, aromatic hydrocarbon resins, aliphatic hydrocarbonresins, and terpene resins. In general, light-colored tackifiersselected from hydrogenated rosin esters, terpenes, or aromatichydrocarbon resins can be used.

Other materials can be added for special purposes, including, forexample, oils, plasticizers, antioxidants, UV stabilizers, pigments,curing agents, polymer additives, and other additives provided that theydo not significantly reduce the optical clarity of the pressuresensitive adhesive.

The provided adhesive compositions may have additional components addedto the precursor mixture. For example, the mixture may include amultifunctional crosslinker. Such crosslinkers include thermalcrosslinkers which are activated during the drying step of preparingsolvent coated adhesives and crosslinkers that copolymerize during thepolymerization step. Such thermal crosslinkers may includemultifunctional isocyanates, aziridines, multifunctional(meth)acrylates, and epoxy compounds. Exemplary crosslinkers includedifunctional acrylates such as 1,6-hexanediol diacrylate ormultifunctional acrylates such as are known to those of skill in theart. Useful isocyanate crosslinkers include, for example, an aromaticdiisocyanate available as DESMODUR L-75 from Bayer, Cologne, Germany.Ultraviolet, or “UV”, activated crosslinkers can also be used tocrosslink the pressure sensitive adhesive. Such UV crosslinkers mayinclude benzophenones and 4-acryloxybenzophenones.

In addition, the precursor mixtures for the provided adhesivecompositions can include a thermal or a photoinitiator. Examples ofthermal initiators include peroxides such as benzoyl peroxide and itsderivatives or azo compounds such as VAZO 67, available from E. I. duPont de Nemours and Co. Wilmington, Del., which is2,2′-azobis-(2-methylbutyronitrile), or V-601, available from WakoSpecialty Chemicals, Richmond, Va., which isdimethyl-2,2′-azobisisobutyrate. A variety of peroxide or azo compoundsare available that can be used to initiate thermal polymerization at awide variety of temperatures. The precursor mixtures can include aphotoinitiator. Particularly useful are initiators such as IRGACURE 651,available from Ciba Chemicals, Tarrytown, N.Y., which is2,2-dimethoxy-2-phenylacetophenone. Typically, the crosslinker, ifpresent, is added to the precursor mixtures in an amount of from about0.05 parts by weight to about 5.00 parts by weight based upon the otherconstituents in the mixture. The initiators are typically added to theprecursor mixtures in the amount of from 0.05 parts by weight to about 2parts by weight. The precursor mixtures can be polymerized and/orcross-linked using actinic radiation or heat to form the adhesivecomposition as described above and in the Examples below.

The pressure-sensitive adhesive precursors can be blended to form anoptically clear mixture. The mixture can be polymerized by exposure toheat or actinic radiation (to decompose initiators in the mixture). Thiscan be done prior to the addition of a cross-linker to form a coatablesyrup to which, subsequently, one or more crosslinkers, and additionalinitiators can be added, the syrup can be coated on a liner, and cured(i.e., cross-linked) by an addition exposure to initiating conditionsfor the added initiators. Alternatively, the crosslinker and initiatorscan be added to the monomer mixture and the monomer mixture can be bothpolymerized and cured in one step. The desired coating viscosity candetermine which procedure used. The disclosed adhesive compositions orprecursors may be coated by any variety of known coating techniques suchas roll coating, spray coating, knife coating, die coating, and thelike. Alternatively, the adhesive precursor composition may also bedelivered as a liquid to fill the gap between the two substrates andsubsequently be exposed to heat or UV to polymerize and cure thecomposition. The thickness of the adhesive layer in the articles ofdisclosure tends to be at greater than about 5 micrometers, greater thanabout 10 micrometers, greater than about 15 micrometers, or even greaterthan about 20 micrometers. The thickness is often less than about 1000micrometers, less than about 250 micrometers, less than about 200micrometers, or even less than about 175 micrometers. For example, thethickness can be from about 5 to about 1000 micrometers, from about 10to about 500 micrometers, from about 25 to about 250 micrometers, orfrom about 50 to about 175 micrometers. The greater the thickness of theadhesive the more cloud point resistant the adhesive has to be in orderto be useful in a display application.

The pressure sensitive adhesive layer may be optically clear. As usedherein, the term “optically clear” refers to a material that has aluminous transmission of greater than about 90 percent, a haze of lessthan about 2 percent, and opacity of less than about 1 percent in the400 to 700 nm wavelength range. Both the luminous transmission and thehaze can be determined using, for example, ASTM-D 1003-95. Typically,the optically clear adhesive may be visually free of bubbles.

The pressure sensitive adhesive layer desirably maintains opticalclarity, bond strength, and resistance to delamination over the lifetimeof the article in which it is used. Whether an adhesive will likely havethese desirable characteristics can be determined using an acceleratedaging test. The pressure sensitive adhesive layer can be positionedbetween two substrates for this test. The resulting laminate is thenexposed to elevated temperatures, optionally, combined with elevatedhumidity conditions, for a period of time. For example, the cloudpoint-resistant pressure sensitive adhesive layer can often retain itsoptical clarity after aging at 90° C. for approximately 500 hourswithout humidity control (i.e., the relative humidity in the oven isusually below about 10 percent or below about 20 percent).Alternatively, the cloud point resistant pressure sensitive adhesive canoften retain its optical clarity after aging at 70° C. for approximately72 hours with a relative humidity of about 90 percent. Most importantly,the cloud point resistant pressure sensitive adhesive can often retainits optical clarity after aging at 70° C. for approximately 72 hourswith a relative humidity of about 90 percent and rapid (i.e. withinminutes) cooling to ambient conditions. After aging, the averagetransmission of the adhesive between 450 nanometers (nm) and 650 nm canbe greater than about 85 percent and the haze can be less than about 2percent.

Laminates are provided that include an optical film or optically clearsubstrate and a cloud point resistant optically clear pressure sensitiveadhesive layer adjacent to at least one major surface of the opticalfilm or substrate. The articles can further include another substrate(e.g., permanently or temporarily attached to the pressure sensitiveadhesive layer), another adhesive layer, or a combination thereof. Asused herein, the term “adjacent” can be used to refer to two layers thatare in direct contact or that are separated by one or more thin layers,such as primer or hard coating. Often, adjacent layers are in directcontact. Additionally, laminates are provided that include a cloud pointresistant pressure sensitive adhesive layer positioned between twosubstrates, wherein at least one of the substrates is an optical film.Optical films intentionally enhance, manipulate, control, maintain,transmit, reflect, refract, absorb, retard, or otherwise alter lightthat impinges upon a surface of the film. Films included in thelaminates include classes of material that have optical functions, suchas polarizers, interference polarizers, reflective polarizers,diffusers, colored optical films, mirrors, louvered optical film, lightcontrol films, transparent sheets, brightness enhancement film,anti-glare, and anti-reflective films, and the like. Films for theprovided laminates can also include retarder plates such as quarter-waveand half-wave phase retardation optical elements. Other optically clearfilms include anti-splinter films and electromagnetic interferencefilters.

In some embodiments, the resulting laminates can be optical elements orcan be used to prepare optical elements. As used herein, the term“optical element” refers to an article that has an optical effect oroptical application. The optical elements can be used, for example, inelectronic displays, architectural applications, transportationapplications, projection applications, photonics applications, andgraphics applications. Suitable optical elements include, but are notlimited to, glazing (e.g., windows and windshields), screens ordisplays, cathode ray tubes, and reflectors.

Exemplary optically clear substrates include, but are not limited to adisplay panel, such as liquid crystal display, an OLED display, a touchpanel, electrowetting display or a cathode ray tube, a window orglazing, an optical component such as a reflector, polarizer,diffraction grating, mirror, or cover lens, another film such as adecorative film or another optical film.

Representative examples of optically clear substrates include glass andpolymeric substrates including those that contain polycarbonates,polyesters (e.g., polyethylene terephthalates and polyethylenenaphthalates), polyurethanes, poly(meth)acrylates (e.g., polymethylmethacrylates), polyvinyl alcohols, polyolefins such as polyethylenes,polypropylenes, and cellulose triacetates. Typically, cover lenses canbe made of glass, polymethyl methacrylates, or polycarbonate.

In other embodiments, the substrate can be a release liner. Any suitablerelease liner can be used. Exemplary release liners include thoseprepared from paper (e.g., Kraft paper) or polymeric material (e.g.,polyolefins such as polyethylene or polypropylene, ethylene vinylacetate, polyurethanes, polyesters such as polyethylene terephthalate,and the like). At least some release liners are coated with a layer of arelease agent such as a silicone-containing material or afluorocarbon-containing material. Exemplary release liners include, butare not limited to, liners commercially available from CP Film(Martinsville, Va.) under the trade designation “T-30” and “T-10” thathave a silicone release coating on polyethylene terephthalate film.

The release liner can be removed to adhere the optical film to anothersubstrate (i.e., removal of the release liner exposes a surface of anadhesive layer that subsequently can be bonded to another substratesurface). Often, the adhesive layer is permanently bonded to this othersubstrate, although in some cases the adhesion may be limited to allowfor reworking of the display.

The laminates have at least one of the following properties: thepressure sensitive adhesive layer has optical transmissivity over auseful lifetime of the article, the pressure sensitive adhesive canmaintain a sufficient bond strength between layers of the article, thepressure sensitive adhesive can resist or avoid delamination, and thepressure sensitive adhesive can resist bubbling of the adhesive layerover a useful lifetime. The resistance to bubble formation and retentionof optical transmissivity can be evaluated using accelerated agingtests. Laminates can often withstand exposure to elevated temperatures(e.g., 60 to 90° C.), optionally, under elevated humidity conditions(e.g., 80 to 90 percent relative humidity), for a period of time (e.g.,1 day to 1 month). In particular the laminates of this disclosuremaintain their low haze and high transmission, even after prolongedexposure to elevated temperatures and elevated humidity (e.g., 60 to 90°C. and 80 to 90 percent relative humidity) followed by a rapid cool downto ambient condition (e.g. cooling to room temperature within minutesafter exposure to the elevated heat and elevated humidity).

The adhesive compositions of the present disclosure may be applieddirectly to one or both sides of an optical element such as a polarizer.The polarizer may include additional layers such as an anti-glare layer,a protective layer, a reflective layer, a phase retardation layer, awide-angle compensation layer, and a brightness enhancing layer. In someembodiments, the pressure sensitive adhesives of the present disclosuremay be applied to one or both sides of a liquid crystal cell. It mayalso be used to adhere a polarizer to a liquid crystal cell. Yet anotherexemplary set of optical laminates include the application of a coverlens to a LCD panel, the application of a touch panel to an LCD panel,the application of a cover lens to a touch panel, or combinationsthereof.

FIG. 1 is a cross sectional illustration of an embodiment of a providedoptically clear laminate. The laminate 100 has cloud point-resistantadhesive composition 104 coated onto substrate 102. Optical film 106 isin contact with adhesive composition 104. The laminate provides anoptically clear, haze resistant optical element.

Objects and advantages of this disclosure are further illustrated by thefollowing examples, but the particular materials and amounts thereofrecited in these examples, as well as other conditions and details,should not be construed to unduly limit this invention.

EXAMPLES Materials

EHA 2-ethylhexyl acrylate NVC N-vinyl caprolactam iBOA isobornylacrylate IRGACURE 2,2-dimethoxy-2-phenylacetophone, a photoinitiator 651available from Ciba Specialty Chemicals, Tarrytown, NY. DESMODUR amultifunctional isocyanate crosslinker, available from L-75 SartomerCompany, Exton, PA. HDDA 1,6-hexanediol diacrylate CD552 monofunctionalmethoxylated polyethylene glycol (550) methacrylate, available fromSartomer. SR9036 ethoxylated (30) bisphenol A dimethacrylate, availablefrom Sartomer. HEA 2-hydroxyethyl acrylate 4HBA 4-hydroxybutyl acrylatePPA6 poly(propylene glycol) acrylate, available as BISOMER PPA6 fromCognis, Germany. VAZO 67 2,2′-azobis(2-methylbuyronitrile), a thermalinitiator available from DuPont. BA butyl acrylate MA methyl acrylateEtOAc ethyl acetate IOTG isooctyl thioglycolate

Accelerated Aging Test Method

Laminates were prepared by bonding a 125 μm thick polyester film(MELINEX 716, available from DuPont Company, Wilmington, Del.) to afloat glass plate using the OCA (175 μm thickness). The laminates wereplaced in an oven set at 70° C./90% relative humidity (RH). After 72hours the laminates were taken out of the oven, cooled down to roomtemperature, and visually observed. In addition to the visualobservation the percent transmission and % haze measurement can also bemade using for example the Byk-Gardner TCS Plus spectrophotometer. Inthis test the same optical laminate described above is used. During thetest, the background is determined using the PET and glass only. Thusthe reported values are for the adhesive only. The adhesive of thisdisclosure typically show less than 5% haze and preferably less than 2%haze after exposure to the accelerated aging test.

In the haze test, “cloudy” means a haze of 10% or more, “slight haze”means a haze value below 5%, and “clear” means a haze value below 2%.

Example 1

A monomer premix was prepared using IRGACURE 651 (0.1 parts), EHA (55parts), iBOA (40 parts), and NVC (5 parts). This mixture was partiallypolymerized under a nitrogen-rich atmosphere by exposure to ultravioletradiation to provide a coatable syrup having a viscosity of about 3000cps (3 PaS). Then HDDA (0.1 part), CD552 (5 parts), and additionalIRGACURE 651 (0.16 parts) were added to the syrup and the syrup wasknife-coated between two silicon-treated release lines at a thickness of175 μm. The resulting coated material was then exposed to low intensityultraviolet radiation (a total energy of 1 J/cm²) having a spectraloutput from 300-400 nm with a maximum at 351 nm. The resulting OCA waslaminated according to the procedure in the Accelerated Aging TestMethod section.

Example 2

The same procedure was used as in Example 1, except after the syrupingprocess, HDDA (0.1 part), CD552 (10 parts), and additional IRGACURE 651(0.16 parts) were used.

Example 3

A 1-L bottle was charged with VAZO67 (0.35 g), BA (58.0 g), MA (40.0 g),HEA (2.0 g), CD552 (20 parts), IOTG (0.2 parts) and toluene (280 g). Thesolution was deaerated with nitrogen bubbling for 10 minutes and wasthen heated at 58° C. in a water bath for 24 hours with agitation. Thenadditional EtOAc (210 g) and toluene (40 g) were added to give a viscoussolution at 20% solids. The solution was mixed with Desmodur L-75 (0.10parts) and placed on a mechanical roller for 30 minutes. The solutionwas then coated on a release liner and dried at 70° C. to a final OCAthickness of 25 μm. A thick OCA sample for testing was made bylaminating seven 25 μm samples together.

Example 4

The same procedure was used as in Example 1, except that HDDA (0.1part), SR9036 (2 parts), and additional IRGACURE 651 (0.16 parts) wereadded to the coatable syrup.

Example 5

The same procedure was used as in Example 1, except that HDDA (0.1part), SR9036 (5 parts), and additional IRGACURE 651 (0.16 parts) wereadded to the coatable syrup.

Example 6

The same procedure was used as in Example 1, except that HDDA (0.1part), HEA (10 parts), and additional IRGACURE 651 (0.16 parts) wereadded to the coatable syrup.

Example 7

The same procedure was used as in Example 1, except that HDDA (0.1part), HEA (20 parts), and additional IRGACURE 651 (0.16 parts) wereadded to the coatable syrup.

Example 8

The same procedure was used as in Example 1, except that HDDA (0.1part), 4HBA (10 parts), and additional IRGACURE 651 (0.16 parts) wereadded to the coatable syrup.

Example 9

The same procedure was used as in Example 1, except that HDDA (0.1part), 4HBA (20 parts), and additional IRGACURE 651 (0.16 parts) wereadded to the coatable syrup.

Example 10

The same procedure was used as in Example 1, except that HDDA (0.1part), BISOMER PPA6 (50 parts), and additional IRGACURE 651 (0.16 parts)were added to the coatable syrup.

Comparative Example 1

The same procedure was used as in Example 1, except that HDDA (0.1 part)and additional IRGACURE 651 (0.16 parts) were added to the coatablesyrup.

Comparative Example 2

The same procedure was used as in Example 3, except that the monomerscharge were BA (58 parts), MA (40 parts), and HEA (2 parts).

Comparative Example 3

The same procedure was used as in Example 1, except that HDDA (0.1part), BISOMER PPA6 (20 parts), and additional IRGACURE 651 (0.16 parts)were added to the coatable syrup.

TABLE 1 Visual Observations of Laminates after 72 hours 70° C./90% RH,cooled to RT) Example OCA Composition Observation 1 EHA/iBOA/NVC/CD552Slight Haze 55//40/5/5 2 EHA/iBOA/NVC/CD552 Clear 55//40/5/10 3BA/MA/HEA/CD552 Clear 58/40/2/20 4 EHA/iBOA/NVC/SR9036 Slight Haze55/40/5/2 5 EHA/iBOA/NVC/SR9036 Clear 55/40/5/5 6 EHA/iBOA/NVC/HEASlight Haze 55/40/5/10 7 EHA/iBOA/NVC/HEA Clear 55/40/5/20 8EHA/iBOA/NVC/4HBA Slight Haze 55/40/5/10 9 EHA/iBOA/NVC/4HBA Clear55/40/5/20 10  EHA/iBOA/NVC/PPA6 Clear 55/40/5/50 CE1 EHA/iBOA/NVCCloudy 55/40/5 CE2 BA/MA/HEA Cloudy 58/40/2 CE3 EHA/iBOA/NVC/PPA6 Cloudy55/40/5/20 CE = Comparative ExampleThe results show that cloudiness (haze) can be reduced by incorporatinghydrophilic moieties in the OCA. This can be achieved through theincorporation of increasing amounts of polymeric hydrophilic compoundssuch as those containing polyethylene oxide (such as, for example, CD552or SR9036) or by using monomers with high hydroxyl equivalent content(such as, for example, 4HBA or HEA).

Various modifications and alterations to this disclosure will becomeapparent to those skilled in the art without departing from the scopeand spirit of this disclosure. It should be understood that thisdisclosure is not intended to be unduly limited by the illustrativeembodiments and examples set forth herein and that such examples andembodiments are presented by way of example only with the scope of thisdisclosure intended to be limited only by the claims set forth herein asfollows.

1. An optically clear laminate comprising: a first substrate having atleast one major surface; a second substrate having at least one majorsurface; and a cloud point-resistant, optically clear adhesivecomposition situated between and in contact with at least one majorsurface of the first substrate and at least one major surface of thesecond substrate, wherein the optically clear adhesive composition isderived from precursors that comprise: from about 75 to about 95 partsby weight of an alkyl acrylate having 1 to 14 carbon in the alkyl group;from 0 to about 5 parts of a copolymerizable polar monomer; and fromabout 1 to about 25 parts of a hydrophilic polymeric compound based upon100 parts of the alkyl acrylate and the copolymerizable polar monomer.2. An optically clear laminate according to claim 1 wherein at least oneof the first substrate and the second substrate are selected from adisplay panel, a touch panel, an optical film, a cover lens, and window.3. An optically clear laminate according to claim 2 wherein the coverlens comprises at least one of glass, polymethylmethacrylate, orpolycarbonate.
 4. An optically clear laminate according to claim 2wherein the display panel is selected from a liquid crystal display, aplasma display, an OLED display, an electrowetting display, and acathode ray tube display.
 5. An optically clear laminate according toclaim 2 wherein the optical film is selected from a reflector, apolarizer, a mirror, an anti-glare or anti-reflective film, ananti-splinter film, a diffuser, or electromagnetic interference filter.6. An optically clear laminate according to claim 1 wherein the alkylacrylate comprises aliphatic, cycloaliphatic, or aromatic alkyl groups.7. An optically clear laminate according to claim 1 wherein the adhesivecomposition comprises an alkyl acrylate that is selected from2-ethylhexyl acrylate, isooctyl acrylate, isobomyl acrylate, butylacrylate, methyl acrylate, and combinations thereof
 8. An opticallyclear laminate according to claim 1 wherein the adhesive compositioncomprises a polar monomer that has functional groups that are selectedfrom carboxylic acids, amides, urethanes, ureas, and lactams.
 9. Anoptically clear laminate according to claim 1 wherein the adhesivecomposition comprises a hydrophilic polymeric compound that comprises atleast one of a poly(ethylene oxide) having at least 10 repeat units,poly(N-vinylpyrrolidone), poly(acrylamide), or a polymer containing atleast one of these segments.
 10. An optically clear laminate accordingto claim 1 wherein the adhesive composition has a thickness of greaterthan about 100 μm.
 11. An optically clear laminate according to claim 1wherein the adhesive composition further comprises a crosslinker.
 12. Anoptically clear laminate according to claim 1 that remains clear afterit is placed in an environment of at least 70° C. and 90% relativehumidity for at least 72 hours, cooled down to room temperature, andthen observed.
 13. An optically clear laminate according to claim 1,wherein the adhesive has a visual light transmission of at least 90% anda haze of no more than 2% after it is placed in an environment of atleast 70° C. and 90% relative humidity for at least 72 hours, cooleddown to room temperature
 14. An optically clear laminate comprising: afirst substrate having at least one major surface; a second substratehaving at least one major surface; and a cloud point-resistant,optically clear adhesive composition situated between and in contactwith at least one major surface of the first substrate and at least onemajor surface of the second substrate, wherein the adhesive compositionis derived from precursors that comprise: from about 60 to about 95parts by weight of an alkyl acrylate having 1 to 14 carbon atoms in thealkyl group; from 0 to about 5 parts of a copolymerizable polar monomer;and from about 5 to about 50 parts of a hydroxyl-containing monomer thathas an OH equivalent weight of less than
 400. 15. An optically clearlaminate according to claim 14 wherein the first substrate, the secondsubstrate, or both the first substrate and the second substrate areselected from a display panel, a touch panel, an optical film, a coverlens, or window.
 16. An optically clear laminate according to claim 15wherein the cover lens comprises at least one of glass,polymethylmethacrylate, or polycarbonate.
 17. An optically clearlaminate according to claim 15 wherein the display panel is selectedfrom a liquid crystal display, a plasma display, an OLED display, anelectrowetting display, and a cathode ray tube display.
 18. An opticallyclear laminate according to claim 15 wherein the optical film isselected from a reflector, a polarizer, a mirror, an anti-glare oranti-reflective film, an anti-splinter film, a diffuser, orelectromagnetic interference filter.
 19. A laminate according to claim16 wherein the adhesive composition has a thickness of greater thanabout 100 μm.
 20. A laminate according to claim 16 that remains clearafter it is placed in an environment of at least 70° C. and 90% relativehumidity for at least 72 hours, cooled down to room temperature, andthen observed.
 21. An optically clear adhesive composition that isderived from precursors that comprise: from about 75 to about 95 partsby weight of an alkyl acrylate having 1 to 14 carbon in the alkyl group;from 0 to about 5 parts of a copolymerizable polar monomer; and fromabout 1 to about 25 parts of a hydrophilic polymeric compound based upon100 parts of the alkyl acrylate and the copolymerizable polar monomer.